Single layer small grain size FePT:C film for heat assisted magnetic recording media

ABSTRACT

FePt-based heat assisted magnetic recording (HAMR) media comprising a thick granular FePt:C magnetic recording layer capable of maintaining a single layer film having desirable magnetic properties. According to one embodiment, the thick granular FePt:C magnetic recording layer comprises a plurality of carbon doped FePt alloy columnar grains, where the plurality of carbon doped FePt alloy columnar grains comprise a carbon gradient along the thickness of the hard magnetic recording layer.

TECHNICAL FIELD

This invention relates to the field of disk drives and more specifically, to heat assisted magnetic recording media for disk drives.

BACKGROUND

For all types of substrates, magnetic recording media has begun to incorporate perpendicular magnetic recording (PMR) technology in an effort to increase areal density and is now working toward densities of 800 Gbits/in². Generally, PMR media may be partitioned into two primary functional regions: a soft magnetic underlayer (SUL) and a magnetic recording layer(s) (RL). FIG. 1 illustrates portions of a conventional perpendicular magnetic recording disk drive system having a recording head 101 including a trailing write pole 102 and a leading return (opposing) pole 103 magnetically coupled to the write pole 102. An electrically conductive magnetizing coil 104 surrounds the yoke of the write pole 102. The bottom of the opposing pole 103 has a surface area greatly exceeding the surface area of the tip of the write pole 102. As the magnetic recording disk 105 is rotated past the recording head 101, current is passed through the coil 104 to create magnetic flux within the write pole 102. The magnetic flux passes from the write pole 102, through the disk 105, and across to the opposing pole 103 to record in the PMR layer 150. The SUL 110 enables the magnetic flux from the trailing write pole 102 to return to the leading opposing pole 103 with low impedance.

Typically, higher areal densities are typically achieved with well-isolated smaller grains in the PMR layer. A higher magnetocrystalline anisotropy constant (K_(u)) is typically required to resist the demagnetization effects of the perpendicular geometry and to keep the smaller grains thermally stable to reduce media noise.

With the advent of heat-assisted magnetic recording (HAMR) media, areal densities of 900 Gbits/in² and higher using PMR technology has been realized. This is because HAMR media comprises of a magnetic compound, such as an FePT alloy, that has a higher magnetic stability than PMR technology using non-HAMR media (e.g., CoPt). However, because the HAMR media comprises of such higher-stability magnetic compounds, HAMR media requires that heat be applied to it before changes its magnetic orientation can be changed. Typically, when PMR technology magnetically records data to HAMR media, it first uses a heating element, such as a laser, to increase the temperature of the recording location on the media, in order to lower the location's high magnetic anisotropy constant (K_(u)) sufficiently to allow a change to its magnetic orientation (i.e., record data).

FIG. 2 illustrates a cross-sectional view of an exemplary heat-assisted magnetic recording (HAMR) media comprising a hard magnetic recording layer 205, a soft magnetic underlayer (SUL) 210, a heatsink layer and non-magnetic interlayer 215 between the hard magnetic recording layer 205 and soft magnetic underlayer 210, and a bottom substrate 225. The hard magnetic recording layer 205 illustrated is a L1 ₀ layer made of iron platinum (FePt), a magnetic compound known to have a high magnetic anisotropy constant (K_(u)). Other suitable compounds for the hard magnetic layer include iron platinum alloys (FePtX), such as FePtCu, FePtAu, FePtAg, and FePtNi. It has been discovered that certain dopants, such as carbon (resulting in FePtX:C), when added to a iron platinum alloy of a hard magnetic recording layer, results in small grain size, granular microstructure, high magnetocrystalline anisotropy, high coercivity, good texture and ordering, and lower ordering temperature, all of which are desirable properties for HAMR media.

Unfortunately, in order to provide strong magnetic signal for the reader sensor detection and high signal-to-noise ratio (SNR) in the recording process, HAMR media require a relatively thick hard magnetic recording layer, preferably a thickness above 5 nm. This is particularly problematic for HAMR media that utilize carbon doped iron platinum alloy (FePtX:C) for its hard magnetic layer, as typically a FePtX:C hard magnetic layer having a thicknesses beyond 5-6 nm results in the formation of two or more layers of FePtX:C. This is clearly shown in FIG. 3A-3C, where FIG. 3A shows a FePt:C recording layer (303) of ˜4.6 nm forming a single layer, where FIG. 3B shows a FePt:C recording layer (306) of ˜7 nm starting to form a second layer, and where FIG. 3C shows a FePt:C recording layer (309) of ˜9.8 nm forming two layers (312 and 315). When more than a single layer forms within the hard magnetic layer, properties required of the HAMR, such as high coercivity, begin to degrade. For example, FIG. 4 illustrates how coercivity for the examples provided in FIGS. 3A-3C begins to degrade as the thickness of the FePt:C recording layer increases.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention is illustrated by way of example, and not limitation, in the figures of the accompanying drawings in which:

FIG. 1 (prior art) illustrates a conventional perpendicular recording disk drive system;

FIG. 2 (prior art) illustrates a cross-sectional view of an exemplary heat-assisted magnetic recording (HAMR) media;

FIGS. 3A-3C provides images depicting the cross-sections of example heat-assisted magnetic recording (HAMR) media, each media having a FePt:C magnetic recording layer of different thickness;

FIG. 4 illustrates the correlation between coercivity and thickness of a FePt:C magnetic recording layer within heat-assisted magnetic recording (HAMR) media;

FIG. 5 illustrates a cross-sectional view of a heat-assisted magnetic recording (HAMR) media comprising a FePtX:C recording layer in accordance with an embodiment of the present invention;

FIG. 6 provides images depicting the cross-sections of two example heat-assisted magnetic recording (HAMR) media, each media having a FePt:C recording layer of the same thickness, but where one media has a FePt:C recording layer in accordance with an embodiment of the present invention;

FIG. 7 provides images depicting the plane view of a heat-assisted magnetic recording (HAMR) media having a FePt:C recording layer in accordance with an embodiment of the present invention;

FIG. 8 illustrates a method of manufacturing a heat-assisted magnetic recording (HAMR) media, in accordance with an embodiment of the present invention; and

FIG. 9 illustrates a disk drive including a heat-assisted magnetic recording (HAMR) recording disk, in accordance with an embodiment of the present invention.

DETAILED DESCRIPTION

In the following description, numerous specific details are set forth, such as examples of specific layer compositions and properties, to provide a thorough understanding of various embodiment of the present invention. It will be apparent however, to one skilled in the art that these specific details need not be employed to practice various embodiments of the present invention. In other instances, well known components or methods have not been described in detail to avoid unnecessarily obscuring various embodiments of the present invention.

The terms “over,” “under,” “between,” and “on” as used herein refer to a relative position of one media layer with respect to other layers. As such, for example, one layer disposed over or under another layer may be directly in contact with the other layer or may have one or more intervening layers. Moreover, one layer disposed between two layers may be directly in contact with the two layers or may have one or more intervening layers. In contrast, a first layer “on” a second layer is in contact with that second layer. Additionally, the relative position of one layer with respect to other layers is provided assuming operations are performed relative to a substrate without consideration of the absolute orientation of the substrate.

Embodiments of the present invention include a recording medium comprising a hard magnetic recording layer disposed above a soft magnetic underlayer, where the hard magnetic recording layer comprises a plurality of carbon doped FePt or FePt alloy (FePtX) columnar grains, and the plurality of carbon doped FePt alloy columnar grains comprise a carbon gradient along the thickness of the hard magnetic recording layer. For some such embodiments, which include either FePt doped with a carbon gradient or FePt alloys (FePtX) doped with a carbon gradient, the hard magnetic recording layer can achieve thicknesses above 5 nm while maintaining a single layer.

FIG. 5 illustrates a cross-sectional depiction of an exemplary embodiment of a HARM media structure 500 comprising a L1 ₀ FePtX:C hard magnetic recording layer 505, having a thickness 506 greater than 5 nm, a granular structure (i.e., columns of FePtX:C 507), small grain size, good uniformity, high coercivity, high magnetic flux and good atomic ordering. Suitable materials X for the FePtX:C alloy of the hard magnetic recording layer 505 may include Ag, Au, B, Cu, Ir, Nb, Ni Ti, W, or Zr.

As illustrated by their shading, the FePtX:C columns 507 of the recording layer 505 comprise a carbon (C) gradient along the thickness 506 of the entire hard magnetic layer 505. In some embodiments, the such a graded columns are created by two or more multiple layers (N>2) of FePtX:C films with varying carbon (C) content in each layer. For example, a gradient may be created using a first layer of FePtX:C film having a carbon (C) content of 40% (i.e., FePtX:C40) disposed over the interlayer and heatsink layer 515, and a second layer of FePtX:C film having a carbon (C) content of 20% (i.e., FePtX:C20) disposed over the first layer of FePtX:C film. It would be well understood by one skilled in the art that layers of FePt:C films having different carbon (C) may also be used to create the hard magnetic recording layer with a carbon gradient, and that FePt and FePtX film layers having carbon content different from those discussed here may also be used.

Also depicted is a substrate 525, that may be, for example, a glass, a metal, and/or a metal alloy material. In a particular embodiment, the substrate 525 is disk-shaped or annular. Glass substrates that may be used include, for example, a silica-containing glass such as borosilicate glass and aluminosilicate glass. Metal and metal alloy substrates that may be used include, for example, aluminum (Al), tantalum (Ta), and aluminum magnesium (AlMg) substrates. in an alternative embodiment, other substrate materials such as polymers and ceramics may be used.

The soft magnetic underlayer (SUL) 510 is disposed over the substrate 525. Generally, the SUL 510 may include any materials known in the art. The SUL 510 itself may be a laminate or multilayer stack of a plurality of soft magnetic layers separated by nonmagnetic or antiferromagnetic films. In one exemplary embodiment, the SUL 510 includes a synthetic antiferromagnet (SAF) structure comprising two amorphous soft ferromagnetic layers (e.g., CoTaZr or CoFeTaZr, etc.) antiferromagnetically coupled with one another across a spacer layer (e.g. ruthenium (Ru)) there-between. The thickness of the SUL 510 will generally be in the range of 5 nm to 60 nm.

Disposed over the soft magnetic underlayer (SUL) 510 is an interlayer and a heatsink layer 515. The heatsink layer 515 specifically facilitates heat transfer for the HAMR media. The heatsinky layer may also be useful in alternative embodiments in accordance with the present invention, including thermally assisted magnetic recording (TAMR) or optically assisted magnetic recording (OAMR)). Although the illustrated example embodiment depicts the heatsink layer 515 is disposed between the SUL 510 and the hard magnetic recording layer 505, it should be appreciated the heatsink layer 515 may alternatively be disposed between the SUL 510 and the substrate 525. Generally, regardless of the position within the media structure 500, the heatsink layer 515 is usually a metal (e.g. Cu) or other heat conductive material. In the exemplary embodiment, the heatsink layer 525 may have a thickness between 30 nm and 100 nm.

Although the illustrated embodiment depicts the heatsink layer 515 is disposed between the SUL 510 and the hard magnetic recording layer 505, it should be appreciated the heatsink layer 515 may alternatively be disposed between the SUL 510 and the substrate 525. Generally, regardless of the position within the media structure, the heatsink layer 515 is a metal or other heat conductive material. In the exemplary embodiment, the heatsink layer 515 may be made of copper (Cu) and have a thickness between 30 nm and 100 nm.

Disposed over the hard magnetic recording layer 505 are a soft magnetic layer 521, an overcoat 530, and a lubricant 535. The soft magnetic layer 521 is disposed over the hard magnetic recording layer 505, and may comprise a CoFe or CoCr based soft magnetic alloy. This soft magnetic may contain: Al, B, C, Cr, Cu, N, Nb, Ni, Re, Ru, Si, Ta and/or Zr.

Overcoat 530 is formed on top of the soft magnetic recording layer 521 to meet tribological requirements such as contact-start-stop (CSS) performance and corrosion protection. Materials usually utilized for the overcoat layer 530 include carbon-based materials, such as hydrogenated or nitrogenated carbon. A lubricant 535 is placed on top of the overcoat layer 530 to further improve tribological performance. Exemplary lubricants include a perfluoropolyether or phosphazene lubricant or a composite thereof.

FIG. 6 provides a transmission electron microscope (TEM) image 603 of the cross-section of a heat-assisted magnetic recording (HAMR) media 612 in accordance with one embodiment of the invention, and a transmission electron microscope (TEM) image 609 of the cross-section of a heat-assisted magnetic recording (HAMR) media 615 in accordance with conventional embodiments. As illustrated, HAMR media 612 comprises of several different layers described above, including a hard magnetic recording layer of 10 nm, comprising of a layer of FePt:C40 and a layer of FePt:C20, thereby resulting in a gradient of carbon content along the thickness of the hard magnetic recording layer. TEM image 603 depicts a single layer of FePt:C forming, despite the thickness of the hard magnetic recording layer being larger than 5 nm.

On the other hand, HAMR media 615 comprises of several different layers described above, including a hard magnetic recording layer of 10 nm, comprising a singe layer of FePt:C40. TEM image 609 depicts a two layers of FePt:C forming, due to the thickness of the hard magnetic recording layer being larger than 5 nm.

FIG. 7 provides transmission electronic microscope (TEM) images depicting the plane view of a heat-assisted magnetic recording (HAMR) media having a FePt recording layer having a carbon gradient in accordance with an embodiment of the present invention. Specifically, the TEM images provided depict the good granular microstructure that results from the FePt recording layer having a carbon gradient.

FIG. 8 illustrates one embodiment of a method 800 of manufacturing a heat assisted magnetic recording disk having a FePtX:C-based PMR media structure such as that described elsewhere herein in reference to FIG. 5. A substrate 525 is generated, or otherwise provided, at operation 810. The generation of a substrate for a magnetic recording disk is per se known in the art; accordingly a detailed discussion is not provided. At operation 815, the SUL 510 including any of the materials described elsewhere herein, such as a CoFe or CoCr based soft magnetic alloy, is deposited over the substrate 525. Any conventional deposition method configured for the formation of the SUL 510 may be utilized, such as sputter deposition (i.e., physical vapor deposition (PVD)).

At operation 820 the interlayer and heatsink layer 515 deposited over the SUL 510 to facilitate heat-assisted perpendicular magnetic recording.

At operation 830, the hard recording layer, comprising two or more layers (N>2) of FePtX:C film, where each film layer has a graded carbon (C) content, is deposited over the interlayer and heatsink layer 515. As discussed above, materials X that can be used in utilized in the FePtX alloy, such as, Ag, Au, B, Cu, Ir, Nb, Ni, Ti, W, or Zr, for example, to stabilize the phase or tune the magnetic properties of the hard magnetic recording layer 505. In some embodiments, the two or more layers of FePtX:C may be deposited using two or more chambers containing FePtX:C material of differing carbon content. For example, to deposit one layer of FePtX:C40 and one layer of FePtX:C20 for the hard magnetic recording layer, one chamber would contain FePtX:C40 material, while another would contain FePtX:C20 material. In some such embodiments, the FePtX:C material is deposited at a pressure between 2 mTorr and 100 mTorr.

At operation 840, a soft magnetic layer 521 is deposited over the hard magnetic recording layer 505. In some embodiments, the soft magnetic layer 521 and the hard magnetic layer 505 may form a graded Hk structure, an exchange coupled composite (FCC) structure or a synthetic antiferromagnetically coupled (SAF) structure. The soft magnetic alloy of the soft magnetic layer 521 may be a FePtX or CoPtX alloy, where X may be Ag, Au, B, Cu, Ir, Nb, Ni, Ti, W, or Zr. In addition, the soft magnetic alloy may also be a disordered structure, having a low anisotropy field and a curie temperature.

Next, in operation 850, an overcoat 530 layer and a lubricant layer 535 are formed over the hard magnetic recording layer 505. Overcoat 530 may be formed on top of the soft magnetic recording layer 521 to meet tribological requirements such as contact-start-stop (CSS) performance and corrosion protection. As discussed above, predominant materials for the overcoat layer 530 are carbon-based materials, such as hydrogenated or nitrogenated carbon. A lubricant 535 may be placed on top of the overcoat layer 530, by dip coating, spin coating, etc., to further improve tribological performance. Example lubricants include a perfluoropolyether or phosphazene lubricant or a composite thereof.

For deposition of each FePtX:C layer of the recording layer 505, a variety of methods known in the art, for example, electroless plating, sputtering (e.g., static or in-line), chemical vapor deposition (CVD), ion-beam deposition (IBD), etc. may be utilized. For example a static sputter systems may be utilized, such as those available from manufacturers such as Intevac Inc. of Santa Clara, California and Carton-Anelva Corp. of Japan. With in-line sputtering systems, disk substrates are loaded on a pallet that passes through a series of deposition chambers the deposit films successively on substrates. In-line sputtering systems are available from manufacturers such as Ulvac Corp. of Japan.

FIG. 9 illustrates a disk drive 900 having disk 901. Disk drive 900 may include one or more disks 900 to store data. Disk 901 resides on a spindle assembly 960 that is mounted to drive housing 980. Data may be stored along tracks in the magnetic recording layer of disk 901. The reading and writing of data is accomplished with head 950 that has both read and write elements. The write element is used to alter the properties of the perpendicular magnetic recording layer of disk 901. In one embodiment, head 950 may have magneto-resistive (MR), or giant magneto-resistive (GMR) elements. In an alternative embodiment, head 950 may be another type of head, for example, an inductive read/write head or a Hall effect head. In some embodiments, the disk 900 has the media structure as depicted in FIG. 5, and the disk drive 900 is a heat assisted magnetic recording (HAMR) drive and incorporate components of a laser source, a waveguide, and a near-field transducer (not depicted). Techniques in generating and focusing a laser beam are known in the art, and thus, are not described in particular detail. A spindle motor (not shown) rotates spindle assembly 960 and, thereby, disk 901 to position head 950 at a particular location along a desired disk track. The position of head 950 relative to disk 901 may be controlled by position control circuitry 970. The use of disk 901 fabricated in the manners discussed above may improve the performance of the perpendicular magnetic recording layer of disk 901 by providing a higher magnetic anisotropy from an L1 ₀-ordered recording layer. The use of disk 901 fabricated in the manners discussed above may also enable the use of L1 ₀-structured media on non-glass substrates.

In the foregoing specification, embodiments of the invention have been described with reference to specific exemplary features thereof. It will, however, be evident that various modifications and changes may be made thereto without departing from the broader spirit and scope of the invention as set forth in the appended claims. The specification and figures are, accordingly, to be regarded in an illustrative rather than a restrictive sense. 

What is claimed is:
 1. A recording medium comprising: a hard magnetic recording layer comprising a plurality of carbon doped FePt alloy columnar grains; a soft magnetic layer disposed over the hard magnetic recording layer, the soft magnetic layer comprising a CoFe or CoCr based soft magnetic alloy; and a soft magnetic underlayer disposed under the hard magnetic recording layer, wherein the hard magnetic recording layer has a thickness that extends perpendicular with respect to the soft magnetic underlayer; wherein the plurality of carbon doped FePt alloy columnar grains comprises a carbon gradient along the thickness of the hard magnetic recording layer.
 2. The recording medium of claim 1, wherein the each of the plurality of carbon doped FePt alloy columnar grains comprises a plurality of overlying sub-layers of the carbon doped FePt alloy, wherein differing carbon content of each overlying sub-layer results in the carbon gradient.
 3. The recording medium of claim 2, wherein the plurality of overlying sub-layers comprises a first overlying sub-layer having 40 at. % carbon.
 4. The recording medium of claim 3, wherein the plurality of overlying sub-layers further comprises a second overlying sub-layer having 20 at. % carbon.
 5. The recording medium of claim 3, wherein the first overlying sub-layer when compared to other ones of the plurality of overlaying sub-layers is positioned closest to the soft magnetic underlayer.
 6. The recording medium of claim 1, wherein the carbon gradient is such that carbon content within the hard magnetic recording layer is greater closer to the soft magnetic underlayer.
 7. The recording medium of claim 1, wherein the carbon gradient is such that carbon content within the hard magnetic recording layer is greater away from the soft magnetic underlayer.
 8. The recording medium of claim 1, wherein the thickness of the hard magnetic recording layer is more than 5 nm.
 9. The recording medium of claim 1, wherein the FePt alloy in the carbon doped FePt alloy columnar grains is a FePtX alloy, where X comprises Ag, Au, B, Cu, Ir, Nb, Ni, Ti, W, or Zr.
 10. The recording medium of claim 1, wherein the thickness of the plurality of carbon doped FePt alloy columnar grains is more than 5 nm.
 11. The recording medium of claim 1, further comprising a heatsink layer under the hard magnetic recording layer and above the soft magnetic underlayer.
 12. A recording device comprising: a housing containing a recording head and a recording medium; the recording head for reading magnetic signals from, and writing magnetic signals to, the recording medium; and the recording medium comprising: a hard magnetic recording layer comprising a plurality of carbon doped FePt alloy columnar grains; a soft magnetic layer disposed over the hard magnetic recording layer, the soft magnetic layer comprising a CoFe or CoCr based soft magnetic alloy; and a soft magnetic underlayer disposed under the hard magnetic recording layer, wherein the hard magnetic recording layer has a thickness that extends perpendicular with respect to the soft magnetic underlayer; wherein the plurality of carbon doped FePt alloy columnar grains comprise a carbon gradient along the thickness of the hard magnetic recording layer.
 13. The recording device of claim 12, wherein the each of the plurality of carbon doped FePt alloy columnar grains comprises a plurality of overlying sub-layers of the carbon doped FePt alloy, wherein differing carbon content of each overlying sub-layer results in the carbon gradient.
 14. The recording device of claim 13, wherein the plurality of overlying sub-layers comprises a first overlying sub-layer having 40 at. % carbon.
 15. The recording device of claim 14, wherein the plurality of overlying sub-layers further comprises a second overlying sub-layer having 20 at. % carbon.
 16. The recording device of claim 14, wherein the first overlying sub-layer when compared to other ones of the plurality of overlaying sub-layers is positioned closest to the soft magnetic underlayer.
 17. The recording device of claim 12, wherein the carbon gradient is such that carbon content within the hard magnetic recording layer is greater closer to the soft magnetic underlayer.
 18. The recording device of claim 12, wherein the carbon gradient is such that carbon content within the hard magnetic recording layer is greater away from the soft magnetic underlayer.
 19. The recording device of claim 12, wherein the thickness of the hard magnetic recording layer is more than 5 nm.
 20. The recording device of claim 12, wherein the FePt alloy in the carbon doped FePt alloy columnar grains is a FePtX alloy, where X comprises Ag, Au, B, Cu, Ir, Nb, Ni, Ti, W, or Zr.
 21. The recording device of claim 12, wherein the thickness of the plurality of carbon doped FePt alloy columnar grains is more than 5 nm.
 22. The recording device of claim 12, further comprising a heatsink layer under the hard magnetic recording layer and above the soft magnetic underlayer. 